Investigation of physical properties of conductive, transparent RF sputtered ITO thin films as a function of thickness and post annealing Temperature. www.ijcm.ir. 2008; 16 (1) :91-98
URL: http://ijcm.ir/article-1-652-en.html
Abstract:   (2078 Views)

Thin films Indium tin oxide (ITO) with various thicknesses, from 130-620nm, have been deposited on the thin glass substrates by RF sputtering using ITO ceramic (90% wt. In2O3 and 10% wt. SnO2) target, and subsequently annealed in vacuum at various temperatures. Electrical and optical characteristics of ITO samples, before and after annealing at different temperatures, were investigated by four point probe and UV/VIS/IR spectrophotometer. Structural properties of layers deposited at optimum temperature of 400˚C were analyzed by XRD. SEM analysis was used to investigate the morphology of the optimal surface layer. Results show that by increasing the thickness, crystalline structure varies, so that sheet resistance, resistivity and transparency of films vary. Layer deposited with 130nm (lower thickness) has 83.71% transmittance and 2.34×10-4Ωcm resistivity. In contrast, 620nm thickness film with 79.07% transparency has the lowest electrical resistivity about 1×10-4Ωcm at 400˚C. This layer can be used as an optimal film with 1.6 Ω/□ sheet resistance for many applications.    

Full-Text [PDF 121 kb]   (668 Downloads)    
Type of Study: Research | Subject: Special

Add your comments about this article : Your username or Email:
CAPTCHA

© 2020 All Rights Reserved | Iranian Journal of Crystallography and Mineralogy

Designed & Developed by : Yektaweb